Quid sunt Martensitic Claustra?
Ictus martensiticus talea genus est componentium renitentium indutorum quae communiter in impactibus comminutoribus utuntur ad materias duras et laesuras opprimendas. Hi vectes ictu ex ferro fabricantur, qui processus curationis caloris specificas sustinent ad microstructuram martensiticam explicandam, quae eas tribuit eximias proprietates ad applicationes opprimendas. Secundum duritiem et duritiem, martensiticum chalybeum ictui vectes sunt alicubi in medio inter vectes duri ictu manganesi et chrome duris vectibus. Cum materia cibaria abrasiva, ictu martensitico vectes clarissimas utilitates praebent cum vectibus manganesorum comparatis, et ictu martensitico vectis minimo utitur magno periculo fracturae consociatae cum usu chromatis vectis. Blow vectes e ferro martensitico usi sunt in secundario contritione et. aliquatenus in tertiariis terendis.
Conditiones applicabiles
Properties: Martensitic chalybs et duritiem et impactionem resistentiae habet proprietates, comparatas cum ferro chrome, non facile fracturam. Praeterea in applicationibus materialibus laesuras schedae martensiticae mallei longiorem vitam habent quam scheda manganesorum malleorum.
Est commendatur;
- Construction vastum
- Adusta calcis
- In casu maximae magnitudinum feed (prout geometriae diverticulum comprimentis)
Gradus et Chemical Compositio
| Grade | Chemical Compositio (%) | ||||||||
| C | Si | Mn | Cr | Mo | Ni | Cu | S | P | |
| 30Mn2CrSi | 0.25 ~ 0.35 | 0.5 ~ 1.2 | 1.2 ~ 2.2 | 0.5 ~ 1.2 | / | / | / | ≤ 0-04 | ≤ 0-04 |
| 30CrMnSiMo | 0.25 ~ 0.35 | 0.5 ~ 1.8 | 0.6 ~ 1.6 | 0.5 ~ 1.8 | 0.2 ~ 0.8 | / | / | ≤ 0-04 | ≤ 0-04 |
| 30CrNiMo | 0.25 ~ 0.35 | 0.4 ~ 0.8 | 0.4 ~ 1.0 | 0.5 ~ 2.0 | 0.2 ~ 0.8 | 0.3 ~ 2.0 | / | ≤ 0-04 | ≤ 0-04 |
| 40CrNiMo | 0.35 ~ 0.45 | 0.4 ~ 0.8 | 0.4 ~ 1.0 | 0.5 ~ 2.0 | 0.2 ~ 0.8 | 0.3 ~ 2.0 | / | ≤ 0-04 | ≤ 0-04 |
| 42Cr2Si2MnMo | 0.38 ~ 0.48 | 1.5 ~ 1.8 | 0.8 ~ 1.2 | 1.8 ~ 2.2 | 0.2 ~ 0.6 | / | / | ≤ 0-04 | ≤ 0-04 |
| 45Cr2Mo | 0.40 ~ 0.48 | 0.8 ~ 1.2 | 0.4 ~ 1.0 | 1.7 ~ 2.0 | 0.8 ~ 1.2 | ≤ 1.5 | / | ≤ 0-04 | ≤ 0-04 |
| 30Cr5Mo | 0.25 ~ 0.35 | 0.4 ~ 1.0 | 0.5 ~ 1.2 | 4.0 ~ 6.0 | 0.2 ~ 0.8 | ≤ 1.5 | / | ≤ 0-04 | ≤ 0-04 |
| 40Cr5Mo | 0.35 ~ 0.45 | 0.4 ~ 1.0 | 0.5 ~ 1.2 | 4.0 ~ 6.0 | 0.2 ~ 0.6 | ≤ 1.5 | / | ≤ 0-04 | ≤ 0-04 |
| 50Cr5Mo | 0.45 ~ 0.55 | 0.4 ~ 1.0 | 0.5 ~ 1.2 | 4.0 ~ 6.0 | 0.2 ~ 0.6 | ≤ 1.5 | / | ≤ 0-04 | ≤ 0-04 |
| 60Cr5Mo | 0.55 ~ 0.65 | 0.4 ~ 1.0 | 0.5 ~ 1.2 | 4.0 ~ 6.0 | 0.2 ~ 0.6 | ≤ 1.5 | / | ≤ 0-04 | ≤ 0-04 |
Nota: Hoc solum vexillum chemica compositio est. Ipsa compositio chemica componi debet secundum condiciones operantis emptoris.
Organizatio metallica et Mechanica Properties
- Duritiem superficiei: 44-57 HRC
- Impulsum fortitudo: 100-300 J/cm²
Nullam justo Martensitic!
Nonnulli clientes non contenti sunt servitio mallei martensitici vita. Ex hac, nostri fabrum novas materias elaboraverunt.series MC (ictus ceramic martensiticus vectes).
Iisdem condicionibus operandis, servitium vita noviter designati vectis ictu augeri potest per 150% ~ 200%.